High photocatalytic activity of hydroxyapatite biodegradable semiconductor for solar panels and environment protection

Incorporating metal ions into a calcium hydroxyapatite structure is a successful pathway to increase their physical, chemical and biological properties. The calcium hydroxyapatite was obtained by solid state method at high temperature, using CaCO3 and (NH4)2HPO4 as sources of calcium and phosphorus. Metal ion (M2+ = Mn2+, Co2+, Ni2+, Cu2+) incorporation was carried out by dint of grinding and high temperature effect for remove all impurity. Hydroxyapatite (HAP) powders doped with metal ions were characterized by uv-visible spectroscopy analysis to evaluate the photocatalytic activity of all samples of hydroxyapatite. The result shows the high photocatalytic activity of all HAP powders.

L’incorporation des ions métalliques dans la structure d’hydroxyapatite de calcium est une voie efficace pour augmenter leurs propriétés physiques, chimiques et biologiques. L’hydroxyapatite de calcium a été obtenue par une voie solide à haute température, en utilisant du CaCO3 et du (NH4)2HPO4 comme sources de calcium et de phosphore. L’incorporation des ions métalliques (M2+ = Mn2+, Co2+, Ni2+, Cu2+) a été réalisée par force de broyage et sous l’effet de la
température élevée pour éliminer toute impureté. Les poudres d’hydroxyapatite (HAP) dopées avec des ions métalliques ont été caractérisées par la spectroscopie Uv-visible pour évaluer l’activité photocatalytique de tous les échantillons de nos poudres d’HAP. Les résultats obtenus montrent une activité photocatalytique élevée dans toutes les poudres HAP.

Hydroxyapatite Cobalt Solar panel Solid state Urbach energy Gap energy Metal ion

Hydroxyapatite Cobalt Panneau solaire Etat solide Energie d’Urbach Energie de gap Ion Métallique