Physics > Home > Entropy: Thermodynamics – Energy – Environment – Economy > Special issue IEES > Article
Ayman Elghoul
Université de Sfax
Tunisia
Akram Krichene
Université de Sfax
Tunisia
Wahiba Boujelben
Université de Sfax
Tunisia
Received : 12 October 2023 / Accepted : 22 December 2023
Published on 26 January 2024 DOI : 10.21494/ISTE.OP.2024.1073
In this work, we have investigated the magnetic and the magnetocaloric properties of polycrystalline Pr0.63A0.07Sr0.3MnO3 (A = Pr, Sm and Bi) prepared by solid-state reaction at high temperature. The magnetic study revealed that all our samples exhibit a ferromagnetic-paramagnetic transition with increasing temperature, with an important magnetocaloric effect near TC. Using theoretical calculations, we have enhanced the magnetocaloric effect for our samples, based on theoretical composites. The obtained composites exhibit important magnetocaloric effect in an extended temperature range, which indicates the possibility of using these composites for magnetic refrigeration.
Dans ce travail, nous avons investigué les propriétés magnétiques et magnétocaloriques des composés polycristallins Pr0,63A0,07Sr0,3MnO3 (A = Pr, Sm et Bi) préparés par la méthode céramique à haute température. L’étude magnétique montre que nos composés montrent une transition ferromagnétique-paramagnétique lorsque la température augmente, avec un effet magnétocalorique important au voisinage de TC. En utilisant des calculs théoriques, nous avons pu améliorer l’effet magnétocalorique pour nos composés en se basant sur des composites théoriques. Les composites obtenus montrent un effet magnétocalorique important sur une large gamme de température, ce qui indique la possibilité d’utiliser ces composites pour la réfrigération magnétique.
Manganite composite magnetic entropy change magnetocaloric effect
Manganite composite variation d’entropie magnétique effet magnétocalorique